Gunning Castables – NK-Teplokhimmontazh Holding
15.10.2017

Gunning Castables

Gunning castables are designed to be applied by gunning.

The structure of the material name is:
NK-Gun Mzzz
NK – COMPANY NAME
GUN – APPLICATION method – gunning.
M – castable with reduced cement content.
ZZZ – Operating temperature, degrees Celsius, divided by 10 (150 = temperature up to 1500° C).

NK-Gun M170 T

Medium-cement shotcrete with working temperature up to 1600 °C – NK-Gun M170 T   Standard technical documents: ТУ 1523-075-22298789-2015 Type: SHOTCRETE Bond: HYDRAULIC Basic material: ALUMINA,  SECAR-71 Application method: GUNNING BASIC PROPERTIES: Maximum operating temperature 1700 °C Apparent density on firing at 1000 °С 3.2 g/cm³ Maximum fraction 5 mm Permanent linear extansion at 1000 Read more about NK-Gun M170 T[…]

NK-Gun M160B

Medium-cement shotcrete with working temperature up to 1600 °C – NK-Gun M160 B   Standard technical documents: ТУ 1523-075-22298789-2015 Type: SHOTCRETE Bond: HYDRAULIC Basic material: ALUMINA,  SECAR-71 Application method: GUNNING BASIC PROPERTIES: Maximum operating temperature 1600 °C Apparent density on firing at 1000 °С 2.9 g/cm³ Maximum fraction 5 mm Permanent linear extansion at 1000 Read more about NK-Gun M160B[…]

SSHVS-1.4t (СШВS-1.4)

Light-weight refractory shotcrete – SSHVS-1.4t (СШВS-1.4)   Standard technical documents: Type: LIGHT-WEIGHT REFRACTORY CASTABLE Bond: HYDRAULIC Basic meterial: LIGHT-WEIGHT CHAMOTTE Application method: GUNNING BASIC PROPERTIES: Maximum operating temperature 1300 °C Long-term operating temperature 1180 °C Apparent density after firing on 1000 оС 1350 kg/m³ CHEMICAL ANALYSIS: Al2O3 41 % CaO 4 % Fe2O3 13 % SiO2 Read more about SSHVS-1.4t (СШВS-1.4)[…]

SSHVS-0.6t (СШВS-0.6т)

Light-weight refractory shotcrete – SSHVS-0.6t (СШВS-0.6т) Standard technical documents: Type: LIGHT-WEIGHT REFRACTORY CASTABLE Bond: HYDRAULIC Basic material: VERMICULITE Application method: GUNNING BASIC PROPERTIES: Maximum operating temperature 1100 °C Apparent density on firing at 1000 °C 0.6 g/cm³ Maximum fraction 3 mm Permanent linear extansion at 1000 °C 0,55 % CHEMICAL ANALYSIS: Al2O3 25.0 % CaO Read more about SSHVS-0.6t (СШВS-0.6т)[…]

NK-Gun M160 A

Medium-cement shotcrete with working temperature up to 1600 °C – NK-Gun M160 A   Standard technical documents: ТУ 1523-075-22298789-2015 Type: SHOTCRETE Bond: HYDRAULIC Basic material: ALUMINA,  SECAR-71 Application method: GUNNING BASIC PROPERTIES: Maximum operating temperature 1650 °C Apparent density on firing at 1000 °С 2.5 g/cm³ Maximum fraction 6 mm Permanent linear extansion at 1000 Read more about NK-Gun M160 A[…]

NK-Gun M150 SM

Medium-cement shotcrete with working temperature up to 1500 °C – NK-Gun M150 Standard technical documents: ТУ 1523-075-22298789-2015 Type: SHOTCRETE Bond: HYDRAULIC Basic material: MULLITE-ALUMINA,  SECAR-71 Application method: GUNNING BASIC PROPERTIES: Maximum operating temperature 1550 °C Apparent density 2.1 г/cm³ Ultimate compressive strength 30 N/mm² Permanent linear shrinkage at 1400 °C 0,3 % CHEMICAL ANALYSIS:  Al2O3 Read more about NK-Gun M150 SM[…]

NK-Gun M140

Low-cement shotcrete with working temperature up to 1400°C – NK-Gun M140 Standard technical documents: ТУ 1523-075-22298789-2015 Type: SHOTCRETE Bond: HYDRAULIC Basic material: MULLITE,  SECAR-71 Application method: GUNNING BASIC PROPERTIES: Maximum operating temperature 1450 °C Apparent density on firing at 1000 °С 2.1 g/cm³ Maximum fraction 6 mm Permanent linear extansion 0,7 % CHEMICAL ANALYSIS:  Al2O3 Read more about NK-Gun M140[…]

NK-Gun M130C

Dense low-cement castable with working temperature up to 1300°C – NK-Gun M130 Standard technical documents: ТУ 1523-075-22298789-2015 Type: DENSE LOW-CEMENT CASTABLE Bond: HYDRAULIC Basic material: CHAMOTTE,  SECAR-71 Application method: GUNNING BASIC PROPERTIES: Maximum operating temperature 1350 °C Apparent density on firing at 1000 °С 1,85 g/cm³ Maximum fraction 6 mm Linear shrinkage at 1300 °С Read more about NK-Gun M130C[…]